Bambu PLA-CF is carbon fiber reinforced PLA with improved stiffness and strength. PLA-CF is easy to print and beginner-friendly like regular PLA.
It is AMS compatible with low clogging risk at high-speed printing. The prints are in matte finish with almost invisible layer lines, which make it suitable for printing general engineering parts or models requiring a better appearance, like bike frames, brackets and toys.
*Shipping Time: 1-2 Weeks*
Product Details
Specifications
Features:
- Carbon Fiber Texture & Minimized Layer Lines
- Improved Mechanical Properties
- Stablized Printing Dimension
- Recommended to dry out before use
- AMS Compatible
- 0.2 mm Nozzle Not Compatible
The addition of carbon fiber gives prints a unique matte finish and effectively hides layer lines, providing a smooth, premium look. Bambu PLA-CF could be paired with any PLA series filament to make your prints more colorful and achieve various texture requirements.
Bambu PLA-CF exceeds the mechanical properties of PLA Matte in XY Bending Strength, Z Bending Strength, XY Bending Modulus, Z Bending Modulus, XY Impact Strength, and Z Impact Strength by between 20% and 115%, making it more suitable for printing models with higher strength requirements.
Not prone to clogging in high-speed printing
Bambu PLA-CF is just as easy to print as regular PLA. It can be printed smoothly and consistently at high speed without clogging.
Bambu PLA-CF is just as easy to print as regular PLA. It can be printed smoothly and consistently at high speed without clogging.
Minimal effort in support removal
Bambu PLA-CF is designed to support itself. It can be removed more easily compared to regular PLA, and still maintains a smooth support surface.
Bambu PLA-CF is designed to support itself. It can be removed more easily compared to regular PLA, and still maintains a smooth support surface.
Bambu Lab PLA-CF
- Drying Settings (Blast Drying Oven):55 °C, 8 h
- Printing and Keeping Container's Humidity:Less than 20% RH (Sealed, with Desiccant)
- Nozzle Temperature:210 - 240 °C
- Bed Temperature (with Glue):35 - 45 °C
- Printing Speed:Less than 200 mm/s
- Density:1.22 g/cm³
- Vicar Softening Temperature:69 °C
- Heat Deflection Temperature:55 °C
- Melting Temperature:165 °C
- Melt Index:3.7 ± 0.6 g/10 min
- Tensile Strength:38 ± 4 MPa
- Breaking Elongation Rate:8.4 ± 3.2 %
- Bending Modulus:3950 ± 190 MPa
- Bending Strength:89 ± 4 MPa
- Impact Strength:23.2 ± 3.7 kJ/m²